JS-AOC Palatal S320T-954AT is an additive, pre-promoted, thixotropic flame retardant unsaturated polyester resin. Utilizing low smoke, low toxicity and high flame retardant technology, this resin has medium viscosity and medium reactivity.
JS-AOC Palatal S320T-954AT is an additive, pre-promoted, thixotropic flame retardant unsaturated polyester resin. Utilizing low smoke, low toxicity and high flame retardant technology, this resin has medium viscosity and medium reactivity.
JS-AOC Palatal S320T-954AT is an additive, pre-promoted, thixotropic flame retardant unsaturated polyester resin. Utilizing low smoke, low toxicity and high flame retardant technology, this resin has medium viscosity and medium reactivity.
JS-AOC Palatal S320T-954AT is characterized by high mechanical strength and good process performance. It is widely used in a variety of self-extinguishing reinforced and non-reinforced products, especially those with high requirements on fire resistance, such as architectural decorative panels, ventilation ducts, transportation tools (railroad vehicles, boats) and electrical shells and parts, etc. It is suitable for hand-laying, spraying, casting and other processes.
Oxygen index 38 GB/T 2406
Smoke density D4 52 GB 8323
Germany (fire/smoke/drip) S4/SR2/ST2 DIN 5510-2
France (fire/smoke) M2/F1 NFF 16-101
* Glass fiber content is approximately 40%, gelcoat type Neogel A 400TV-F-1.
| performances | realm | unit (of measure) | Test Standards |
|---|---|---|---|
| exterior condition | turbidity | – | TM 2265 |
| Viscosity 23℃ | 450-550 | mPa.s | TM 2013 |
| inherent | 74-77 | % | TM 2033 |
| Gel time, 25-35°C | 22-28 | minutes | TM 2625 |
Note: Reactivity at 25°C: 1.5g M50 (AKZO-Nobel) in 100g resin
| Performance indicators | numerical value | unit (of measure) | Test Standards |
|---|---|---|---|
| Storage period (unprimed, dark) | 3 | moon | – |
| Performance indicators | numerical value | unit (of measure) | Test Standards |
|---|---|---|---|
| tensile strength | 55 | MPa | ISO 527-2 |
| Tensile modulus of elasticity | 8000 | MPa | ISO 527-2 |
| Elongation at break | 0.7 | % | ISO 527-2 |
| bending strength | 80 | MPa | ISO 178 |
| Bending modulus of elasticity | 7500 | MPa | ISO 178 |
| impact strength | 6.0 | KJ/m² | ISO 179 |
| heat distortion temperature | 90 | ℃ | ISO 75A |
| barcolithic hardness | >40 | – | – |