JS-P13 Resin is unsaturated with DCPD, cashry, and standard diol as its main raw materials. Polyester resin, which has been soluble in the styrene crosslinker, has lower viscosity and medium Reaction activity.
JS-P13 Resin is unsaturated with DCPD, cashry, and standard diol as its main raw materials. Polyester resin, which has been soluble in the styrene crosslinker, has lower viscosity and medium Reaction activity.
JS-P13 resin has high strength, good rigidity, heat -resistant and water -resistant, and excellent glass fiber reinforced mechanical Performance, moderate stretching speed, suitable for pulling craftsmanship cable bridge, thread grooves, roads Road protective fences, cooling tower fillers, grilles and other ordinary profiles.
| Property | Value | Unit | TM |
| Appearance | Yellow transparent viscous liquid | – | – |
| Acid Value | 16-22 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.45-0.55 | Pa.s | GB/T 7193-2008 |
| Solid Content | 67-74 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel time | 8-14 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | There are no defects of casting body | – | – |
| Barcol Hardness | 40 | – | GB/T 3854-2005 |
| HDT | 85 | ℃ | GB/T 1634-2004 |
| Break Elongation | 2.0 | Mpa | GB/T 2567-2008 |
| Tensile Strength | 55 | Mpa | GB/T 2567-2008 |
| Tensile Modulus | 3200 | Mpa | GB/T 2567-2008 |
| Flexural Strength | 90 | Mpa | GB/T 2567-2008 |
| Flexural Modulus | 3200 | Mpa | GB/T 2567-2008 |
1. JS-P13 resin does not contain wax, does not contain promotional agents and tactile additives.
2.JS-P13 resin is sensitive to light, and it is easy to gel after seeing light. Therefore, it is necessary to avoid opening the packaging or exposing it in a strong light before use.
3. Recommended by the curing system: 0.5-2.0%of the BPO curing agent; 0.5-1.5%of TBPB curing agents. The actual selection should be confirmed according to factors such as equipment, products, process temperature, and piercing speed.
4. In view of the differences in compatibility of different resins and different color slurry (pigment paste), customers should deal with the compatibility and stability of the resin and color pulp (pigment paste) before use.