JS-601-1 resin is Orthophthalic type unsaturated polyester resin mainly composed of phthalic anhydride, maleic anhydride, and standard diols. It is soluble in styrene crosslinked monomers and has low viscosity and high reactivity.
JS-601-1 resin is Orthophthalic type unsaturated polyester resin mainly composed of phthalic anhydride, maleic anhydride, and standard diols. It is soluble in styrene crosslinked monomers and has low viscosity and high reactivity.
JS-601-1 resin has light color, good transparency, excellent toughness, and fast curing, making it suitable for ordinary molded grilles and transparent grilles and other products.
| Property | Value | Unit | TM |
| Appearance | Light yellow transparent viscous liquid | – | – |
| Acid Value | 20-26 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.35-0.45 | Pa.s | GB/T 7193-2008 |
| Solid Content | 64-72 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel time | 8-10 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Barcol Hardness | 67 | – | GB/T 3584-2005 |
| Flexural Strength | 380 | Mpa | GB/T 1449-2005 |
| Flexural Modulus | 18000 | Mpa | GB/T 1449-2005 |
| Tensile Strength | 330 | Mpa | GB/T 1447-2005 |
| Tensile Modulus | 16000 | Mpa | GB/T 1447-2005 |
| Property | Value | Unit | TM |
| Appearance | No defects in the casting body | – | – |
| Barcol Hardness | 35 | – | GB/T 3854-2005 |
| HDT | 60 | ℃ | GB/T 1634-2004 |
| Break Elongation | 50 | % | GB/T 2567-2008 |
| Flexural Strength | 2700 | Mpa | GB/T 2567-2008 |
| Flexural Modulus | 12 | Mpa | GB/T 2567-2008 |
| Tensile Strength | 2500 | Mpa | GB/T 2567-2008 |
| Tensile Modulus | 800 | Mpa | GB/T 2567-2008 |
JS-601-1 resin does not contain wax, accelerators, and thixotropic additives
Or do you require assistance in selecting the right formulation for your project?